Collagen fiber membrane-derived chemically and mechanically durable superhydrophobic membrane for high-performance emulsion separation
Journal of Leather Science and Engineering volume 3, Article number: 20 (2021)
Abstract
Developing high-performance separation membrane with good durability is a highly desired while challenging issue. Herein, we reported the successful fabrication of chemically and mechanically durable superhydrophobic membrane that was prepared by embedding UiO-66 as size-sieving sites within the supramolecular fiber structure of collagen fiber membrane (CFM), followed by the polydimethylsiloxane (PDMS) coating. The as-prepared CFM/UiO-66(12)/PDMS membrane featured capillary effect-enhanced separation flux and homogeneous porous channels guaranteed high separation efficiency. When utilized as double-layer separation membranes, this new type of composite membranes separated various surfactant stabilized water-in-oil microemulsions and nanoemulsions, with the separation efficiency high up to 99.993 % and the flux as high as 973.3 L m− 2 h− 1. Compared with commercial polytetrafluoro ethylene (PTFE) membrane, the advantage of the double-layer CFM/UiO-66(12)/PDMS membranes in separation flux was evident, which exhibited one order of magnitude higher than that of commercial PTFE membrane. The CFM/UiO-66(12)/PDMS membrane was acid-alkali tolerant, UV-aging resistant and reusable for emulsion separation. Notably, the CFM/UiO-66(12)/PDMS membrane was mechanically durable against strong mechanical abrasion, which was still capable of separating diverse water-in-oil emulsions after the abrasion with sandpaper and assembled as double-layer separation membranes. We anticipate that the combination of CFM and metal organic frameworks (MOFs) is an effective strategy for fabricating high-performance separation membrane with high mechanical and chemical durability.
Graphical Abstract
![](http://media.springernature.com/lw685/springer-static/image/art%3A10.1186%2Fs42825-021-00060-5/MediaObjects/42825_2021_60_Figa_HTML.png)
1 Introduction
Emulsification technology has been widely utilized in a variety of industrial processes [1,2,3,4], which inevitably generates a large quantity of surfactant-containing emulsion wastewater. The emulsion wastewater has to be treated before discharged. Among various emulsion separation approaches, membrane separation has attracted great interests due to its high separation efficiency and simple separation process [5,6,6,8]. Membrane separation based on size-sieving strategy can be described by the Hagen-Poiseuille equation: J = επrp2Δp/(8µL), where the flux (J) is proportional to the square of radius (rp2) and inversely proportional to the thickness of the membrane (L) [9]. Normally, there is a trade-off effect for size-sieving membrane since the permeation flux is constrained by the small membrane pore size that is a necessity for separating emulsions with extremely small droplets. To address this issue, current strategy to improve the permeation flux heavily relies on decreasing the membrane thickness as much as possible [10]. Unfortunately, ultrathin membranes usually suffer from weak mechanical strength, which compromise their application [11]. Therefore, it is highly desirable to develop new separation membranes that are capable of exhibiting high separation performances and still providing good mechanical strength.
Leather, prepared from the tanning of skins/hides, has been utilized as the raw material for shoes, clothes and gloves for thousands of years due to its outstanding mechanical strength [12, 13]. The tensile strength of leather reaches up to 38 MPa [14], and the tear strength attains 78 N mm− 1 [15]. Leather is formed by supramolecular self-assembly of type I collagen molecules, which actually can be considered as a type of mechanical durable natural membrane (i.e. collagen fiber membrane, CFM) that features a hierarchically fibrous structure from nanoscale to microscale and macroscale. Our previous investigations have verified that the supramolecular fiber structure of type I collagen molecules exhibited the merits of capillary effect enhanced liquid transport kinetics [16]. In consideration of that type I collagen molecules are the component of CFM, CFM is therefore a promising substrate for fabricating mechanical durable and high-performance separation membranes. However, the poly-dispersed pore size of CFM could fail to separate emulsions with small droplet size because the voids among the fibers of CFM can be considerably larger than the particle size of emulsion droplets to be separated, which are tend to directly penetrate the CFM without demulsification. Metal organic frameworks (MOFs), composed of an inorganic metal center and organic linkers [17], have showed great potential in diverse applications, such as gas separation, gas storage and catalysis [18,19,20]. Besides large specific surface area and high porosity, the homogeneous porous structure with controllable pore-size makes MOFs as a promising demulsifying component for both microemulsions and nanoemulsions.
Herein, we synthesized a new type of superhydrophobic composite membrane by embedding MOFs as size-sieving sites within the three dimensional (3D) supramolecular fiber structure of CFM, followed by polydimethylsiloxane (PDMS) coating. Specifically, the UiO-66 grown on CFM by seeding growth method was employed as the size-sieving sites since the UiO-66 has high chemical stability and the micropore size of UiO-66 is ~ 6.0 Å, which is capable of demulsifying both microemulsions and nanoemulsions efficiently [21, 22]. For the CFM embedded with UiO-66 (denoted as CFM/UiO-66), a subsequent PDMS coating was applied to reduce the surface energy and to enhance chemical and mechanical strength, thus obtaining superhydrophobicity and strengthened chemical and mechanical durability. We prepared a series of the CFM/UiO-66(x)/PDMS membranes, where x (h) is the time of seeding growth of UiO-66. The as-prepared superhydrophobic CFM/UiO-66(12)/PDMS membrane exhibited the water contact angle of 158.7o. The double-layer CFM/UiO-66(12)/PDMS membranes demonstrated a remarkable capacity to separate a variety of surfactants stabilized water-in-oil microemulsions and nanoemulsions with efficiencies higher than 99.99 %, including Span 80/SDBS stabilized water-in-dodecane nanoemulsion (NE1), Span 80/CTAB stabilized water-in-dodecane nanoemulsion (NE2), Tween 80/SDBS stabilized water-in-n-octane nanoemulsion (NE3), Tween 80/SDS stabilized water-in-n-heptane nanoemulsion (NE4), Span 80/SDS stabilized water-in-dodecane microemulsion (ME1), and Span 80/CTAB stabilized water-in-dodecane microemulsion (ME2). The separation flux of the double-layer CFM/UiO-66(12)/PDMS membranes was superior to that of commercial polytetrafluoro ethylene (PTFE) membrane. When applied for the separation of NE4, the separation flux of the double-layer CFM/UiO-66(12)/PDMS membranes was as high as 973.3 L m− 2 h− 1, which was 3.18-fold to the flux of commercial PTFE membrane (305.6 L m− 2 h− 1). For the separation of NE1, the flux of the double-layer CFM/UiO-66(12)/PDMS membranes (540.4 L m− 2 h− 1) was one magnitude higher than that of commercial PTFE membrane (77.6 L m− 2 h− 1). Moreover, the double-layer CFM/UiO-66(12)/PDMS membranes were able to be reused for emulsion separation, with separation efficiency high up to 99.993 % in the 5th separation cycle of NE2. The CFM/UiO-66(12)/PDMS membranes remained superhydrophobic after subjected to harsh environments, such as organic solvent immersion, ultraviolet irradiation, strong acid immersion and strong alkali immersion. Notably, the double-layer CFM/UiO-66(12)/PDMS membranes assembled by two CFM/UiO-66(12)/PDMS membranes that were treated by abrasion with sandpaper for 200 cycles still exhibited high-performance separation capability in separating above 6 type of microemulsions and nanoemulsions, with the separation flux as high as 1012.2 L m− 2 h− 1 and the efficiency high up to 99.993 %. Therefore, we provided a new strategy for developing chemically and mechanically durable membrane that was highly efficient for high-performance separation of water-in-oil emulsions.
2 Experimental section
2.1 Materials
Chrome tanned split-leather was supplied by Ruixing Leather Co., Ltd (Haining, China). ZrCl4 (≥ 99.9 %), zirconium (IV) propoxide solution (70wt %) and 1,4-benzenedicarboxylic acid (H2BDC) were purchased from Aladdin Reagent Co. (Shanghai, China). Polydimethylsiloxane (PDMS) prepolymer (Sylgard 184A) and curing agent (Sylgard 184B) were purchased from Dow Corning Corporation (Midland, USA). The PDMS solution was prepared by dissolving 10 g of Sylgard 184A in 200 g dodecane and 1.0 g of Sylgard 184B in 20 g dodecane, followed by mixing above solutions together. Sodium dodecyl benzene sulfonate (SDBS), sodium dodecyl sulfate (SDS), hexadecyl trimethyl ammonium bromide (CTAB), and other chemicals were analytical grade reagents and were used as received without further purification.
2.2 Synthesis of UiO-66 nanoparticles
UiO-66 nanoparticles (UiO-66NPs) were prepared according to the literature[23]. ZrCl4 (0.318 g) was ultrasonically dissolved in 108 mL of N, N-Dimethylformamide (DMF), followed by the addition of H2BDC (0.228 g). The mixture was transferred into an autoclave, heated at 120 °C for 24 h, and then cooled to room temperature. The UiO-66NPs were obtained after centrifuged at 8000 rpm, and dried under vacuum at 60 °C.
2.3 Fabrication of the CFM/UiO-66(x)/PDMS membrane
The collagen fiber membrane (CFM), with the diameter of 8.0 cm and the thickness of 1.5-1.8 mm was immersed in 100 mL of aqueous suspension containing 20 mg of above synthesized UiO-66NPs under ultrasonication for 1.0 h to obtain the seeded CFM. Then, the seeded CFM was dried at 60 °C. DMF (70 mL), zirconium (IV) propoxide solution (0.71 mL) and glacial acetic acid (40 mL) were mixed, followed by the addition of H2BDC (750 mg). Then, the seeded CFM was immersed in above mixture, keeping still for the seeding growth of UiO-66. The resultant products were CFM/UiO-66(x), where x (h) is the time of seeding growth of UiO-66, equaling to 3.0, 6.0, 9.0, 12, 15 and 18. The dried CFM/UiO-66(x) membranes were immersed in 30 mL of 5.0wt% PDMS solution for 5.0 min. After dried at 70 °C, the CFM/UiO-66(x)/PDMS membranes were obtained.
2.4 Fabrication of the CFM/PDMS membrane
The CFM with the diameter of 8.0 cm and the thickness of 1.5-1.8 mm was immersed in 30 mL of 5.0wt% PDMS solution for 5.0 min. After dried at 70 °C, the CFM/PDMS membrane was obtained.
2.5 Preparation of water-in-oil emulsion
Various emulsions with droplet sizes from micrometer to nanometer range were prepared. Table S1 summarizes the ingredients of the prepared six types of emulsions, including Span 80/SDBS stabilized water-in-dodecane nanoemulsion (denoted as NE1), Span 80/CTAB stabilized water-in-dodecane nanoemulsion (denoted as NE2), Tween 80/SDBS stabilized water-in-n-octane nanoemulsion (denoted as NE3), and Tween 80/SDS stabilized water-in-n-heptane nanoemulsion (denoted as NE4), Span 80/SDS stabilized water-in-dodecane microemulsion (denoted as ME1), and Span 80/CTAB stabilized water-in-dodecane microemulsion (denoted as ME2). For the preparation of NE1, Span 80 (0.12 g) and SDBS (0.06 g) were dissolved in dodecane (300 mL) and water (3.0 mL), respectively. The SDBS water solution was drop-wise added into the Span 80 dodecane solution under agitation at 1000 rpm. Then, the resultant mixture was stirred at 2000 rpm for 1.0 h to obtain NE1. Other emulsions were prepared by the similar method used for preparing NE1.
2.6 Emulsion separation of the CFM/UiO-66(x)/PDMS membrane
Emulsion separation was conducted in an H-type equipment (as shown in Figure S1), with the CFM/UiO-66(x)/PDMS membranes fixed between the feed cell and the collecting cell. The prepared emulsion was poured into the feed cell and the corresponding filtrate was obtained in the collecting cell. The water content in the collected filtrates was measured by Karl Fischer moisture titrator (Wo Ye technology, S-300, China). The separation efficiency was calculated by the following equation: Efficiency = 100 %-C, where C is the water content in the filtrate. The flux is calculated as below: J = V/(St), where J is the flux of the membrane, V is the filtrating volume, S is the area of the membrane, and t is the time used for emulsion separation.
The reusability of the double-layer CFM/UiO-66(12)/PDMS membranes was evaluated by repeated separation of NE2 for five cycles. Each separation cycle of NE2 was carried out for 1.0 h, with the flux and water content in the filtrates calculated at the interval of 20 min. After each cycle, the used membranes were washed with ethanol, dried and then applied in the next cycle.
2.7 Chemical and mechanical durability
The solvent resistance of the CFM/UiO-66(12)/PDMS membranes was tested by direct immersion in different solvents. Specifically, the CFM/UiO-66(12)/PDMS membranes were immersed in dodecane, n-heptane or n-octane for 24 h. Then, the treated CFM/UiO-66(12)/PDMS membranes were dried at 70 °C and their water contact angles (WCAs) were measured.
The acid-alkali resistance was also investigated by immersing the CFM/UiO-66(12)/PDMS membranes in the aqueous solution with the pH ranging from 2 to 12. Then, the CFM/UiO-66(12)/PDMS membranes were dried at 70 °C and their WCAs were measured.
The UV resistance of the CFM/UiO-66(12)/PDMS membrane was tested by exposing it to ultraviolet irradiation for 24 h, followed by WCA test. The power of the UV lamp was 18 W, and the maximum wavelength was 365 nm.
The mechanical durability of the CFM/UiO-66(12)/PDMS membrane was examined by abrasion test. The abrasion test was performed on a rub fastness tester (Figure S2). The CFM/UiO-66(12)/PDMS membrane was fixed on the sample table, and a sandpaper (36 mesh, 1.5 cm × 1.5 cm) was stuck on the fixed arm. One cycle of abrasion was defined as a forth-and-back friction of the CFM/UiO-66(12)/PDMS membrane against the sandpaper with a total friction distance of 12 cm. The WCAs of the CFM/UiO-66(12)/PDMS membranes abraded by 50, 100, 150 and 200 abrasion cycles were measured. The double-layer CFM/UiO-66(12)/PDMS membranes assembled by two membranes that were treated by abrasion with sandpaper for 200 cycles were used for separating a series of water-in-oil microemulsions and nanoemulsions, including NE1, NE2, NE3, NE4, ME1 and ME2.
2.8 Characterization
The crystalline structures of UiO-66 and membranes were confirmed by the X-ray diffraction (XRD, Bruker D8 ADVANCE A25X) with Cu Kα radiation. The surface morphologies of UiO-66 and membranes were observed by a field emission scanning electron microscopy (FESEM, Nova Nanosem 450, America) operated at 3.0 kV. Dynamic light scattering (DLS) was measured by the particle size analyzer (Brook haven, NanoBrook, America) for nanoemulsions and the stereomicroscope (Leica, M205 C, Germany) for microemulsions, respectively. Water contents in the filtrates were measured by a Karl Fischer moisture titrator (Wo Ye technology, S-300, China). The wettability of membranes was investigated by water contact angle (Krüss, DSA30, Germany).
3 Results and discussion
The schematic illustration in Fig. 1a shows the preparation of the CFM/UiO-66(12)/PDMS membrane (see the preparation details in the Experimental Section). The CFM was simply immersed in aqueous suspension containing UiO-66 nanoparticles (UiO-66NPs) under ultrasonication. In this way, the UiO-66NPs were embedded into the 3D fibrous network of CFM, which served as seeds for the further growth of UiO-66 size-sieving sites. As shown in Fig. 1b, f, the CFM has a full fibrous 3D supramolecular fiber structure that has the basic building blocks of collagen nanofiber (50–200 nm) with the typical 67 nm D-periodicity. As for the seeded CFM, the UiO-66NPs with the average diameter of 70 nm have been successfully embedded onto the surface of the CFM (Fig. 1c, g). The seeded CFM was further immersed into H2BDC-contained zirconium (IV) propoxide solution for the seeding growth of UiO-66NPs. As shown in Fig. 1d, h, the UiO-66NPs with larger particle size (120 nm) and higher density have been grown on the seeded CFM. These grown UiO-66NPs not only served as the efficient size-sieving sites for emulsion separation but also enhanced the roughness of CFM, which allowed for obtaining superhydrophobicity after a subsequent PDMS coating was applied. After the seeding growth of UiO-66NPs, the resultant CFM/UiO-66(12) membrane was coated with PDMS to reduce the surface energy. As shown in Fig. 1e, i, the UiO-66NPs shows no obvious appearance after the PDMS coating.
Schematic illustration showing the fabrication of the CFM/UiO-66(12)/PDMS membrane (a), FESEM images of CFM (b), the seeded CFM (c), the CFM/UiO-66(12) membrane (d) and the CFM/UiO-66(12)/PDMS membrane (e), the higher magnification images of CFM (f), the seeded CFM (g), the CFM/UiO-66(12) membrane (h) and the CFM/UiO-66(12)/PDMS membrane (i), XRD patterns of simulated UiO-66, the as-synthesized UiO-66, the seeded CFM and the CFM/UiO-66(12) (j) and the digital photograph of the CFM/UiO-66(12)/PDMS membrane (inset: the corresponding WCA) (k)
The successful preparation of the CFM/UiO-66(12) membrane was also confirmed by XRD patterns (Fig. 1j). The XRD pattern of UiO-66NPs synthesized and used as seeds shows high consistence with that of simulated UiO-66 [23]. As for the seeded CFM, the corresponding XRD pattern shows the crystal planes of (111) and (200) of UiO-66. After the seeding growth, the obtained CFM/UiO-66(12) membrane shows the diffraction peaks of (111), (200), (222), (400), (442), and (711) crystal planes of the UiO-66. Moreover, the peak intensity of (111) and (200) crystal planes significantly increases as compared with that of the seeded CFM. Above XRD results indicate the successful seeding and seeding growth of UiO-66NPs on the CFM. For the CFM/UiO-66(12)/PDMS membrane, the mapping images of O, Zr and Si elements confirm the successful growth of UiO-66NPs and the coverage with PDMS layer (Figure S3). The CFM/UiO-66(12)/PDMS membrane exhibits excellent hydrophobicity, with a water contact angle (WCA) of 158.7° (Fig. 1k), which is essential for the separation of water-in-oil emulsions.
We prepared a series of the CFM/UiO-66(x)/PDMS membranes, where x was the seeding growth time (h) of UiO-66NPs, varied from 3.0 to 18. The as-prepared CFM/UiO-66(x)/PDMS membranes were further applied in the separation of Span 80/SDBS stabilized water-in-dodecane nanoemulsion (NE1), and we also fabricated the CFM/PDMS membrane without embedding UiO-66NPs as the size-sieving sites. The single-layer CFM/UiO-66(x)/PDMS membranes were firstly utilized in the separation of NE1. As shown in Figure S4, the filtrate collected through the CFM/PDMS membrane is evidently turbid, which suggests that the CFM/PDMS membrane is incapable of separating NE1 without the presence of UiO-66NPs. As the CFM is modified by UiO-66NPs with the seeding growth time increased from 3.0 to 9.0 h, the dynamic light scattering (DLS) curves of the corresponding filtrates exhibit an obvious shift of the particle size range, from 991–1369 nm to 305–459 nm (Figure S5). Evidently, the seeding growth of UiO-66NPs on the seed CFM is a time-dependent process, which enhances the separation capability of the CFM/UiO-66(x)/PDMS membrane with a longer growth time. Figure S6 shows the difference in the turbidity of the filtrates obtained by the CFM/UiO-66(x)/PDMS membranes. When the seeding growth time is shorter than 12 h, the filtrates separated by the CFM/UiO-66(x)/PDMS membranes are cloudy. The filtrates are almost transparent when the CFM/UiO-66(x)/PDMS membranes (x = 12, 15, 18) are used for NE1 separation, which is consistent with their increased emulsion separation capability.
DLS curves of NE1 before (a) and after the separation by the double-layer CFM/UiO-66(x)/PDMS membranes that were prepared by seeding growth of UiO-66NPs for: 3.0 h (b), 6.0 h (c), 9.0 h (d) and 12 h (e), respectively, fluxes and separation efficiencies to NE1 separated by the double-layer CFM/UiO-66(x)/PDMS membranes with different seeding growth time of UiO-66NPs (f)
Since the single-layer CFM/UiO-66(x)/PDMS membranes were unable to separate NE1 completely, we applied the double-layer CFM/UiO-66(x)/PDMS membranes for separating NE1. As the seeding growth time of UiO-66NPs increases from 3.0 to 9.0 h, the particle size distributions of the collected filtrates separated by the double-layer CFM/UiO-66(x)/PDMS membranes shift from 452–697 nm to the smaller particle size distribution of 95–129 nm (Fig. 2b-d). In the separation of NE1 with the double-layer CFM/UiO-66(12)/PDMS membranes, no particle size distribution is detected in the DLS curve of collected filtrate (Fig. 2e). The corresponding water content is 81.6 ppm and the separation efficiency is as high as 99.992 % (Fig. 2f). These results indicate that the NE1 has been successfully separated by the double-layer CFM/UiO-66(12)/PDMS membranes. The double-layer CFM/UiO-66(15)/PDMS membranes and the CFM/UiO-66(18)/PDMS membranes are also capable of separating NE1, with the separation efficiencies higher than 99.99 % (Fig. 2f). However, the separation fluxes of the double-layer CFM/UiO-66(15)/PDMS membranes (510.3 L m− 2 h− 1) and the CFM/UiO-66(18)/PDMS membranes (502.6 L m− 2 h− 1) are lower than that of the double-layer CFM/UiO-66(12)/PDMS membranes (540.4 L m− 2 h− 1) (Fig. 2f). As a result, the double-layer CFM/UiO-66(12)/PDMS membranes were employed for the separation of the following microemulsions and nanoemulsions.
We envisaged that the difference in separation performances among the double-layer CFM/UiO-66(x)/PDMS membranes should be attributed to the varied amount of UiO-66NPs embedded on the CFM. We compared the field emission scanning electron microscopy (FESEM) images of the CFM/UiO-66(3), CFM/UiO-66(12) and CFM/UiO-66(18) membranes. As shown in Figure S7a, when the seeding growth time of UiO-66NPs is 3.0 h, relatively fewer UiO-66NPs are embedded on the surface of the CFM/UiO-66(3). Due to the inefficient size-sieving sites of UiO-66NPs, the emulsion droplets can directly penetrate through the double-layer CFM/UiO-66(3)/PDMS membranes, thus failing to separate the emulsion. As the seeding growth time of UiO-66NPs increases to 12 h, the UiO-66NPs grown on the CFM become larger and denser (Fig. 1d). Accordingly, the separation capability of the double-layer CFM/UiO-66(12)/PDMS membranes is enhanced sufficiently to separate the emulsion. As the UiO-66NPs continuously grow for 18 h with larger particle size and denser packing, the pathway through the micro channels of UiO-66NPs will enlarge mass transfer resistance and decrease the separation flux (Figure S7b). We proposed a size-sieving mechanism for the separation of water-in-oil emulsions by the double-layer CFM/UiO-66(12)/PDMS membranes. The micropore size of UiO-66 is ~ 6.0 Å, which is smaller than the particle size of emulsion droplets, thus facilitating the demulsification of water-in-oil emulsion droplets. After the demulsification, the permeation of water phase is strictly prevented by the superhydrophobic double-layer CFM/UiO-66(12)/PDMS membranes while the selective permeation of oil phase through the superhydrophobic double-layer CFM/UiO-66(12)/PDMS membranes is allowed.
A variety of mixed surfactant-stabilized water-in-oil microemulsions and nanoemulsions. were separated by the double-layer CFM/UiO-66(12)/PDMS membranes to evaluate their separation performances to other water-in-oil emulsions. As shown in Fig. 3a-c, Figure S8, the double-layer CFM/UiO-66(12)/PDMS membranes are capable of efficiently separating diverse nanoemulsions, including Span 80/CTAB stabilized water-in-dodecane nanoemulsion (NE2), Tween 80/SDBS stabilized water-in-n-octane nanoemulsion (NE3) and Tween 80/SDS stabilized water-in-n-heptane nanoemulsion (NE4). The double-layer CFM/UiO-66(12)/PDMS membranes are also able to separate microemulsions. As shown in Fig. 3d, the droplets of Span 80/SDS stabilized microemulsion (ME1) can be clearly observed under the optical microscopy. In contrast, no emulsion droplets are found in the filtrate collected through the double-layer CFM/UiO-66(12)/PDMS membranes (Fig. 3f). As shown in Figure S9, the separation of double-layer CFM/UiO-66(12)/PDMS membranes to Span 80/CTAB stabilized water-in-dodecane microemulsion (ME2) is also achieved. The separation fluxes of NE2, NE3, NE4, ME1 and ME2 separated by the double-layer CFM/UiO-66(12)/PDMS membranes are 504.6 L m− 2 h− 1, 969.8 L m− 2 h− 1, 973.3 L m− 2 h− 1, 545.4 L m− 2 h− 1 and 351.1 L m− 2 h− 1, respectively (Fig. 3g). The water contents in the filtrates of NE2, NE3, NE4, ME1 and ME2 separated by the CFM/UiO-66(12)/PDMS are 85.1 ppm, 83.1 ppm, 84.8 ppm, 84.1 ppm and 69.4 ppm, respectively, with the corresponding separation efficiencies of 99.991 %, 99.992 %, 99.992 %, 99.992 and 99.993 %, respectively (Fig. 3h).
DLS curves of NE2 before (a) and after (c) the filtration through the double-layer CFM/UiO-66(12)/PDMS membranes, digital photograph of the H-shaped separation device for NE2 separation (b), optical microscopy images of ME1 before (d) and after (f) the filtration through the double-layer CFM/UiO-66(12)/PDMS membranes, digital photograph of the H-shaped separation device for ME1 separation (e), separation fluxes of the double-layer CFM/UiO-66(12)/PDMS membranes to NE1, NE2, NE3, NE4, ME1 and ME2 (g) and the corresponding water contents in the filtrate and separation efficiencies (h), separation fluxes of NE2 obtained during the 5 cycles of separation by using the double-layer CFM/UiO-66(12)/PDMS membranes (i), separation efficiencies of NE2 obtained during the 5 cycles of separation by using the double-layer CFM/UiO-66(12)/PDMS membranes (j)
We also compared the separation performance of the double-layer CFM/UiO-66(12)/PDMS membranes to that of commercial polytetrafluoro ethylene (PTFE) membrane. The commercial PTFE membrane is superhydrophobic with a WCA of 156.5°, as shown in Figure S10. When commercial PTFE membrane is applied in NE1 separation, the separation efficiency in the filtrate collected by the commercial PTFE membrane is 99.990 % which is comparable to that of the CFM/UiO-66(12)/PDMS membrane (99.992 %). However, the flux obtained by the double-layer CFM/UiO-66(12)/PDMS membranes (540.4 L m− 2 h− 1) is one order of magnitude higher than that of commercial PTFE membrane (77.6 L m− 2 h− 1). For the separation of NE4, the separation efficiency of the filtrate separated by commercial PTFE membrane (99.991 %) is comparable to that the double-layer CFM/UiO-66(12)/PDMS membranes (99.992 %). The flux of the double-layer CFM/UiO-66(12)/PDMS membranes for NE4 separation (973.3 L m− 2 h− 1) is 3.18-fold to that of commercial PTFE membrane (305.6 L m− 2 h− 1). These results indicate that the separation capability of the double-layer CFM/UiO-66(12)/PDMS membranes is superior to that of commercial PTFE membrane, which should be mainly ascribed to the capillary effect-enhanced separation flux of CFM.
We evaluated the reusability of the double-layer CFM/UiO-66(12)/PDMS membranes for separation of NE2. The double-layer CFM/UiO-66(12)/PDMS membranes were applied in the continuous separation of NE2 for 60 min, which were regenerated by immersing in 30 mL of ethanol for 10 min, and subsequently reused for the next cycle. During the 5 cycles of NE2 separation, the separation fluxes maintain at a relatively high level (116.4-443.4 L m− 2 h− 1), and the corresponding separation efficiencies are as high as 99.990-99.993 % (Fig. 3i, j). These results manifest the good reusability of the double-layer CFM/UiO-66(12)/PDMS membranes.
The WCAs of the CFM/UiO-66(12)/PDMS membrane before and after exposed to different harsh environments for 24 h (a), the WCAs of the CFM/UiO-66(12)/PDMS membrane immersed in aqueous solutions at varied pH (2–12) for 24 h (b) (inset in b shows the digital photographs of 30 µL of water droplets at pH2–12 on the surface of the CFM/UiO-66(12)/PDMS membrane), digital photographs of water droplets (30 µL) on the surface of the CFM/UiO-66(12)/PDMS membrane abraded with sandpaper for 200 cycles (c), the WCAs of the CFM/UiO-66(12)/PDMS membrane abraded with sandpaper for different cycles (d), separation fluxes of the double-layer CFM/UiO-66(12)/PDMS membranes assembled by two membranes that were treated by abrasion with sandpaper for 200 cycles to NE1, NE2, NE3, NE4, ME1 and ME2 (e), the corresponding water contents in the filtrates and the corresponding separation efficiencies(f)
In practical applications, the membranes may confront the harsh environmental conditions, such as organic solvent, ultraviolet irradiation, as well as strong acid and alkali solutions. Therefore, it is essential to evaluate the chemical durability of the CFM/UiO-66(12)/PDMS membrane. The solvent resistance of the CFM/UiO-66(12)/PDMS membranes was investigated by immersing them in dodecane solution, n-heptane solution or n-octane solution. As shown in Fig. 4a, the superhydrophobicity of membranes is still maintained after the immersion treatment, with the corresponding WCAs all higher than 150°. The inset in Fig. 4b shows the digital photographs of 30 µL of water droplets at pH2–12 on the surface of the CFM/UiO-66(12)/PDMS membrane. The water droplets at pH2–12 can stably stand on the surface of the CFM/UiO-66(12)/PDMS membrane. The acid-alkali resistance of the membranes was further explored by immersing them in acid or alkali solution for 24 h, with the corresponding WCAs higher than 150° (Fig. 4b). Then, the CFM/UiO-66(12)/PDMS membranes were immersed in the solutions at pH2 (for 2.0 h) and pH12 (for 2.0 h), respectively. The membranes immersed in the solution at pH2 (or pH12) were further assembled as the double-layer CFM/UiO-66(12)/PDMS membranes and applied in NE1 separation. No obvious decrease in flux or separation efficiency was observed when the double-layer membranes were applied in the separation of NE1 (Figure S11). These results indicate the good acid-alkali resistance of the CFM/UiO-66(12)/PDMS membrane. Evaluation of UV-aging resistance is also important since a non-negligible decrease of hydrophobicity has been reported after some superhydrophobicity surfaces (e.g. hydrocarbons and fluoroalkyl) are exposed to ultraviolet irradiation [24]. The WCA of the CFM/UiO-66(12)/PDMS membrane remains above 150o after treated by ultraviolet irradiation for 24 h (Fig. 4a). The chemical durability of the CFM/UiO-66(12)/PDMS membrane is attributed to the protection of PDMS coating and the high chemical stability of UiO-66. In addition, the mechanical durability of the CFM/UiO-66(12)/PDMS membrane was also evaluated after subjected to 200 cycles of abrasion. The water droplet maintains the spherical shape on the abraded surface of the CFM/UiO-66(12)/PDMS membrane, showing similar shape to that of water droplet on the intact surface of the CFM/UiO-66(12)/PDMS membrane (Fig. 4c). During the abrasion process, the WCAs of the CFM/UiO-66(12)/PDMS membranes maintain above 150° (Fig. 4d), indicating the durable superhydrophobicity. When the double-layer CFM/UiO-66(12)/PDMS membranes assembled by two CFM/UiO-66(12)/PDMS membranes that were treated by abrasion with sandpaper for 200 cycles were further applied in separating above water-in-oil emulsions (NE1, NE2, NE3, NE4, ME1 and ME2), no obvious loss of fluxes or separation efficiencies were observed (Fig. 4e, f).
4 Conclusions
In summary, we have successfully fabricated a new type of chemically and mechanically durable superhydrophobic membrane by modifying hierarchically fibrous structured CFM with UiO-66, followed by the PDMS coating. The CFM substrate played the essential role to provide mechanical strength and simultaneously enhanced the transmission of liquids. The UiO-66 served as the size-sieving sites to strengthen the separation ability of CFM. The double-layer CFM/UiO-66(12)/PDMS membranes efficiently separated various mixed surfactant-stabilized water-in-oil emulsions under gravity. The separation efficiencies were higher than 99.99 %, and the separation flux reached as high as 973.3 L m− 2 h− 1, showing evident advantage of separation flux as compared with the commercial polytetrafluoro ethylene membrane. Moreover, the superhydrophobic membrane exhibited good reusability, remarkable chemical stability and mechanical durability. Our research demonstrated a new route for developing high-performance and durable separation membrane system.
Availability of data and materials
Not applicable.
Change history
06 May 2023
A Correction to this paper has been published: https://doi.org/10.1186/s42825-023-00121-x
References
Ashrafizadeh SN, Motaee E, Hoshyargar V. Emulsification of heavy crude oil in water by natural surfactants. J Pet Sci Eng. 2012;86:137–43.
Pei L, Wu P, Liu J, Wang J. Effect of nonionic surfactant on the micro-emulsifying water in silicone media. J Surfact Deterg. 2017;20:247–54.
Cheng J, Yu Y, Zhu M. Enhanced biodegradation of sugarcane bagasse by clostridium thermocellum with surfactant addition. Green Chem. 2014;16:2689–95.
Glavac Nk, Lunder M. Preservative efficacy of selected antimicrobials of natural origin in a cosmetic emulsion. Int J Cosmet Sci. 2018;40:276–84.
Zhu Y, Wang J, Zhang F, Gao S, Wang A, Fang W. Zwitterionic nanohydrogel grafted PVDF membranes with comprehensive antifouling property and superior cycle stability for oil-in-water emulsion separation. Adv Funct Mater. 2018;28:1804121.
Li HJ, Cao YM, Qin JJ, Jie XM, Wang TH, Liu JH, Yuan Q. Development and Characterization of Anti-Fouling Cellulose Hollow Fiber UF Membranes for Oil-Water Separation. J Membr Sci. 2006;279:328–35.
Padaki M, Murali RS, Abdullah MS, Misdan N, Moslehyani A, Kassim MA. Membrane technology enhancement in oil-water separation: a review. Desalination. 2015;357:197–207.
Crick CR, Gibbins JA, Parkin IP. Superhydrophobic polymer-coated copper-mesh: membranes for highly efficient oil-water separation. J Mater Chem A. 2013;19:5943–8.
Gao S, Shi Z, Zhang W, Zhang F, Jin j. Photoinduced superwetting single-walled carbon Nanotube/TiO2 ultrathin network films for ultrafast separation of oil-in-water emulsions. ACS Nano. 2014;8:6344–52.
Gao S, Zhu Y, Zhang F, Jin J. Superwetting polymer-decorated SWCNT composite ultrathin films for ultrafast separation of oil-in-water nanoemulsions. J Mater Chem A. 2015;3:2895–902.
Striemer CC, Gaborski TR, McGrath JL, Fauchet PM. Charge- and size-based separation of macromolecules using ultrathin silicon membranes. Nature. 2007;445:749–53.
Deng D, Tang R, Liao X, Shi B. Using collagen fiber as a template to synthesize hierarchical mesoporous alumina fiber. Langmuir. 2008;24:368–70.
Navarro D, Wu J, Lin W, Fullana-i-Palmer P, Puig R. Life cycle assessment and leather production. J Leather Sci Eng. 2020;2:1–13.
Han Y, Hu J, Jiang L. Collagen skin, a water-sensitive shape memory material. J Mater Chem B. 2018;6:5144–52.
Wells HC, Sizeland KH, Kirby N, Hawley A, Mudie S, Haverkamp RG. Collagen fibril structure and strength in acellular dermal matrix materials of bovine, porcine, and human origin. ACS Biomater Sci Eng. 2015;1:1026–38.
Xiao H, Cui Y, Wang Y, Li H, Chen G, Huang X, Shi B. Synergistic combination of the capillary effect of collagen fibers and size-sieving merits of metal-organic frameworks for emulsion separation with high flux. Ind Eng Chem Res. 2020;59:14925–34.
Furukawa H, Cordova KE, O’Keeffe M, Yaghi OM. The chemistry and applications of Metal-Organic frameworks. Science. 2013;341:1230444.
He J, Zhang Y, Pan Q, Yu J, Ding H, Xu R. Three metal-organic frameworks prepared from mixed solvents of DMF and HAc. Microporous Mesoporous Mat. 2006;90:145–52.
James SL. Metal-organic frameworks. Chem Soc Rev. 2003;32:276–88.
Liu H, Liu Y, Li Y, Tang Z, Jiang H. Metal-Organic framework supported gold nanoparticles as a highly active heterogeneous catalyst for aerobic oxidation of alcohols. J Phys Chem C. 2010;114:13362–9.
DeStefano MR, Islamoglu T, Garibay SJ, Hupp JT. Room-Temperature synthesis of UiO-66 and thermal modulation of densities of defect sites. Chem Mater. 2017;29:1357–61.
Cavka JH, Jakobsen S, Olsbye U, Guillou N, Lamberti C, Bordiga S, Lillerud K. P. A new zirconium inorganic building brick forming metal organic frameworks with exceptional stability. J Am Chem Soc. 2008;130:13850–1.
Chen C, Chen D, Xie S, Quan H, Luo X, Guo L. Adsorption behaviors of organic micropollutants on zirconium metal-organic framework UiO-66: analysis of surface interactions. ACS Appl Mater Interfaces. 2017;9:41043–54.
Xiu YH, Hess DW, Wong CP. UV and thermally stable superhydrophobic coatings from Sol-Gel processing. J Colloid Interface Sci. 2008;326:465–70.
Acknowledgements
We thank the financial supports provided by the National Natural Science Funds for Excellent Youth Scholars (No. 21922808), the National Key Research and Development Program (No. 2018YFC1901101), the Fok Ying Tong Education Foundation for Young Teachers in the Higher Education Institutions of China (No. 161099), the National Natural Science Foundation of China (No. 21978176), the 1000 Talents Program of Sichuan Province and the Program of Sichuan University Featured Research Groups in Engineering Disciplines.
Funding
National Natural Science Funds for Excellent Youth Scholars (No. 21922808), the National Key Research and Development Program (No. 2018YFC1901101), the Fok Ying Tong Education Foundation for Young Teachers in the Higher Education Institutions of China (No. 161099), the National Natural Science Foundation of China (No. 21978176) and the 1000 Talents Program of Sichuan Province.
Author information
Authors and Affiliations
Contributions
Xin Huang and Bi Shi conceived the idea. Huifang Li and Wan Zheng carried out materials preparation. Huifang Li and Hanzhong Xiao carried out emulsion separation. Huifang Li, Baicun Hao and Yujia Wang carried out materials characterization. Huifang Li, Wan Zheng, Xin Huang and Bi Shi drafted the manuscript. All authors analyzed the experimental results. The author(s) read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, H., Zheng, W., Xiao, H. et al. Collagen fiber membrane-derived chemically and mechanically durable superhydrophobic membrane for high-performance emulsion separation. J Leather Sci Eng 3, 20 (2021). https://doi.org/10.1186/s42825-021-00060-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s42825-021-00060-5