Combination tanning mechanism inspired environmentally benign catalyst for efficient degradation of tetracycline

Collagen and Leather volume 5, Article number: 22 (2023) Cite this article

Abstract

The utilization of chelation reaction between metals and tannins is a common tanning method in leather chemistry. Herein, a novel combination tanning mechanism inspired environmentally benign catalyst (CMBT-Fe0) was synthesized by immobilizing Fe nanoparticles onto bayberry tannin (BT) grafted chitosan microfibers (CM). The obtained catalyst featured a well-defined microfibrous structure, on which Fe0 nanoparticles were highly dispersed to exhibit exceptional catalytic activity for the degradation of tetracycline (TC). The catalytic activity of CMBT-Fe0 was 1.72 times higher than that of the commercial Fe0 nanoparticles without immobilization, with 95.03% of TC degraded within 90.0 min. The CMBT-Fe0 catalysts were recycled 6 times, with the removal rate of TC maintained at 82.56%. Furthermore, a possible mechanism responsible for the catalytic removal of TC was provided by analyzing the catalytic degradation products via liquid chromatography-mass spectrometry. Therefore, our investigation successfully developed efficient catalysts to address the concerned environmental issue of antibiotic pollution.

Graphical Abstract

1 Introduction

Tetracycline (TC) is one of the broad-spectrum antibiotics that have been widely used in human therapy and veterinary medicine [1]. TC discharged in wastewater could cause a series of negative influences to human health and ecological safety, including a variety of toxic effects, bacterial antibiotic resistance [2, 3]. Various technologies have been developed to deal with TC pollution in water, such as adsorption, electron pulse radiolysis, photocatalysis and biological methods [4,5,6,7]. Among them, nanoscale zero-valent iron (Fe0) technology has emerged as one of the most promising alternatives due to its high efficiency, affordability, and non-toxic nature [8, 9].

Fe0 catalysts are able to degrade various antibiotics via either a Fenton-like oxidation mechanism or a reduction mechanism [10, 11]. However, the agglomeration and Fe3+ leakage of Fe0 catalysts unfortunately result in a loss of reactivity and hinder their interactions with surrounding media [12, 13]. Various inorganic and organic supporting matrices have been investigated to stabilize Fe0 nanoparticles, such as diatomite [14], bentonite [15], PVP [16], polydopamine [17], carboxymethyl cellulose [18] and starch [19]. However, physical interactions with the inorganic supporting matrices are usually ineffective to prevent the aggregation or leaching of Fe0 nanoparticles, while the organic polymers cannot solve the problems such as over encapsulation-caused low activity of catalytic sites, which often leads to poor catalytic performances [20,21,22,23]. To overcome these disadvantages, a novel multifunctional support matrix is required to stabilize Fe0 nanoparticles in an appropriate manner. In this regard, natural polymer materials with abundant functional groups and unique molecular configurations are promising alternatives.

Chitosan is a natural polymer material abundant in hydroxyl and amino groups, which is produced from the deacetylation of chitin, the second most abundant polysaccharide in nature after cellulose [24]. Chitosan has excellent biocompatibility and biodegradability, which is able to be processed into chitosan microfibers (CM) to gain efficient mass transport kinetics [25]. Therefore, CM is a promising matrix to immobilize Fe0 nanoparticles for developing heterogeneous Fe0 nanoparticle catalysts. However, CM is soluble in dilute acids, which requires the improvement of stability in solutions [26]. Moreover, it is preferred to enhance the affinity of CM to metal species for preventing any migration and agglomeration of Fe0 nanoparticles.

Vegetable tannins are a class of water-soluble polyphenols with the molecular weight in the range of 500–3000 Da, which are rich in various plant biomasses, such as leaves, roots and barks. Vegetable tannins are multifunctional natural polymers due to their abundant phenolic hydroxyl groups, which enable them to display high affinity towards metal ions via chelation [27]. Actually, vegetable tannins are utilized as tanning agents with the combination of metals in the leather industry. The as-developed combination tanning methods have been conventionally utilized in leather manufacture, which taken the advantage of the chelation ability of vegetable tannins with metal ions (e.g., Al3+) for significantly enhancing the bridged linkage degree of tanned leather. Great efforts have been dedicated to developing combination tanning techniques [28]. These previous investigations to combination tanning inspired us that the remarkable chelation-based affinity of vegetable tannins to metal ions species is possible to be applied in realizing the immobilization of metal species, such as Fe0 nanoparticles with the high dispersity onto the supporting matrix of CM.

Based on the above idea, bayberry tannin (BT), a typical condensed tannin, was utilized to modify chitosan microfibers (CM). The 6 and 8 positions of the A rings of BT exhibited high nucleophilic reaction activities, which allowed their covalent bonding to the amino groups of CM via reactions with aldehydes (e.g., glutaraldehyde) [29]. The resulting CMBT (chitosan microfibers modified with bayberry tannin) well preserved the well-defined fibrous structure, which further realized the impregnation of Fe3+ via the chelation with BT covalently bound on the surface of CM. Moreover, the covalent-bond interactions between BT and CM inhibited the dissolution of CM in acid solutions, providing with significantly enhanced material stability. After the reduction of Fe3+ on the CMBT, a novel environmentally benign catalyst, CMBT supported Fe0 nanoparticles (CMBT-Fe0) was successfully prepared (Scheme 1). We systematically investigated the performances of CMBT-Fe0 for the catalytic removal of TC, including the effect of initial pH, initial concentration of TC and temperature. Moreover, the catalytic degradation mechanism of TC by the CMBT-Fe0 was also discussed.

Scheme 1
scheme 1

Schematic illustration showing the synthesis procedure of CMBT-Fe0

Full size image

2 Experimental sections

2.1 Materials

Chitosan microfibers were received from Tianjin Glory Tang Technology Co., Ltd. (China). Bayberry tannin was obtained from the plant of forest product in Guangxi province (China). Iron (III) chloride hexahydrate (FeCl3·6H2O), sodium borohydride (NaBH4), tetracycline (TC), commercial Fe0 nanoparticles and all of other chemicals were of analytical grade, which were purchased from Aladdin Co., Ltd. (China). Deionized water was used throughout the experiments.

2.2 Preparation of CMBT-Fe0

1.60 g of bayberry tannin was dissolved in 100.0 mL of deionized water. 4.0 g of chitosan fibers were immersed in the above tannin solution and stirred at 25 °C for 2 h. Subsequently, 5.0 mL of glutaraldehyde solution (v/v, 50%) was added into the above mixture at pH 6.0, which was then reacted for 6.0 h at 40 °C. After the solid–liquid separation and washing, the collected solids were dried at 60 °C for 24 h to obtained CMBT.

0.55 g CMBT was added into 30.0 mL of Fe3+ solution (FeCl3·6H2O, 16.70 mg/mL) at 25 °C and stirred for 90 min. Then 12.0 mL of NaBH4 (10.00 mg/mL) solution was slowly dropwised into the above mixture. After stirring for 1.0 h, the CMBT-Fe0 was separated, followed by washing with distilled water and subsequent drying.

2.3 Catalytic degradation experiments

The catalyst dose was fixed at 55.0 mg for all degradation experiments. The influences of experimental conditions on the degradation of TC were investigated by changing several key parameters, including the initial pH of antibiotic solution (2.0–9.0), the initial concentration of TC (40.0–120.0 mg/L) and temperature (288–303 K). The sample was collected by a disposable syringe, which was then filtered using filterable membrane (0.22 μm). The concentration of TC in the collected filtrate was measured by a UV–Vis spectrophotometer.

2.4 Characterization

The materials morphologies were observed by scanning electron microscope (SEM, Hitachi 4700, Japan). X-ray diffraction (XRD) patterns of CMBT-Fe0 before and after the utilization for degradation of TC were recorded on a Philips-X’ Pert Pro MPD (Netherlands). The X-ray photoelectron spectrum (XPS, Shimadzu ESCA-850, Japan) of samples was recorded by using Mg-Ka X-rays. XPS data were fitted by mixed Gaussian–Lorentzian functions (XPS PEAK 4.1 software). Transmission electron microscopy (TEM) images of samples were characterized using a JEOL 1200 EX-II microscope. The surface functional groups in CM, CMBT, CMBT-Fe3+ and CMBT-Fe0 before and after the utilization for degradation of TC were investigated by the Fourier transform infrared spectrometer (FTIR 920, Tianjin). The concentration of Fe3+ in solutions was detected by an inductively coupled plasma atomic emission spectrometer (ICP-AES, PerkinElmer Optima 2100 DV, USA).

3 Results and discussion

SEM observations shown in Fig. 1a, b confirm that the fibrous morphology of CM was well retained in the CMBT. As shown in Fig. 1c, the Fe0 particles in the CMBT-Fe0 were well-dispersed on the surface of CMBT without significant aggregation, maintaining the fibrous morphology. The successful stabilization and dispersion of Fe0 onto the CMBT are also confirmed by SEM–EDS data (Fig. 1e). The fibrous morphology of CMBT-Fe0 after degradation of TC was well preserved (Fig. 1d). Most importantly, SEM–EDS image of CMBT-Fe0 after degradation of TC (Fig. 1f) indicates that the presence of CMBT effectively prevents the agglomeration of Fe0 particles by the rigid benzene ring skeleton and the phenolic hydroxyl groups of BT. To verify the stability of CMBT under acidic conditions, CM and CMBT were immersed in 0.2 mol/L HCl solutions for 24 h (Additional file 1: Fig. S1). CM was found to dissolve in the HCl solution. In contrast, the fibrous morphology of CMBT was maintained due to the modification of BT. These results manifest that the modification of BT to CM not only effectively suppresses the aggregation and detachment of Fe0 particles but also improves the stability of CM under acidic conditions.

Fig. 1
figure 1

SEM images of CM (a), CMBT (b), CMBT-Fe0 (c), CMBT-Fe0 after the degradation of TC (d) and the SEM–EDS Fe mapping images of CMBT-Fe0 before (e) and after (f) the degradation of TC

Full size image

The TEM images of CMBT-Fe0 before and after degradation of TC are shown in Fig. 2. The Fe0 nanoparticles are highly dispersed in the CMBT-Fe0 before and after the degradation of TC, which confirmed the critical role of BT for the stabilization of Fe0 nanoparticles. These results are consistent with the SEM analyses discussed above. As shown in Fig. 2c, the Fe0 nanoparticles exhibit well-defined lattices, with a lattice spacing of 0.2307 nm. Typical lattice spacing of Fe0 nanoparticles was still observed in the CMBT-Fe0 after the degradation of TC [30].

Fig. 2
figure 2

TEM images of CMBT-Fe0 before (a–c) and after (d–f) the degradation of TC

Full size image

FT-IR spectra of CM, CMBT, CMBT-Fe3+, CMBT-Fe0 and CMBT-Fe0* (the used CMBT-Fe0 after the degradation of TC) are shown in Fig. 3a. In the spectrum of CM, the strong broad peak at 3438.84 cm−1 corresponds to the stretching of O–H and N–H. The peaks observed at 2921.49 cm−1 and 2876.49 cm−1 refer to the bending vibration of C–H. Amide I and II peaks are observed at 1653.33 cm−1 and 1383.03 cm−1, respectively. The peak at 1159.28 cm−1 represents C–O–C stretching, while the peaks at 1081.92 cm−1 and 1029.79 cm−1 are attributed to C–O stretching and skeletal vibration of C-O stretching, respectively. In the spectrum of CMBT, the strong peak intensity at 3438.91 cm−1 is due to the presence of phenolic hydroxyls of BT covalently bound onto CM. The peak at 1456.91 cm−1 refers to the skeleton vibration of benzene ring of BT molecule. The peak at 1379.82 cm−1 belongs to the in-plane bending vibration absorption peak of the phenolic hydroxyls in BT molecule. These results indicate the successful modification of CM with BT [31, 32]. In fact, the colour of CM is changed from white to brown after the modification with BT by utilizing the glutaraldehyde as the bridging agent.

Fig. 3
figure 3

FT-IR (a) and Fe 2p XPS spectra of CMBT-Fe0 before (b) and after (c) degradation of TC. (CMBT-Fe0* in a means the obtained CMBT-Fe0 after the degradation of TC)

Full size image

Compared with the FT-IR spectrum of CMBT, only a new peak located at 607.26 cm−1 corresponding to the stretching vibration of Fe–O was observed in that of CMBT-Fe0 spectrum. The FT-IR spectra of CMBT-Fe3+ and CMBT-Fe0 showed no obvious change, indicating that the majority of functional groups containing in the CMBT are preserved after the reduction of Fe3+ to Fe0 [33].

The elemental valence state of CMBT-Fe0 before and after the degradation of TC were analyzed by XPS (Fig. 3b, c and Additional file 1: Fig. S2). The XPS survey scan spectrum reveals that the CMBT-Fe0 is mainly composed of Fe, C, N and O. In Fig. 3b, the peaks at 710.16 and 711.53 eV are attributed to Fe2O3 and FeOOH, respectively, which suggests that the surface of Fe0 nanoparticles was oxidated during the drying process [34, 35]. The iron in the hydrolyzed state gradually increased in the CMBT-Fe0 after degradation of TC (Fig. 3c), which could be explained by Eq. (1).

$${\text{Fe}}^{{{3} + }} + {\text{ 2H}}_{{2}} {\text{O}} \to {\text{FeOOH }} + {\text{ 2H}}^{ + }$$
(1)

Figure 4a illustrates the influences of initial pH on the catalytic removal performances of TC. It was found that the removal rate of TC is gradually decreased with the increased pH value. 95.03% of TC was successfully removed from the solution after 90.0 min at pH 3.0, whereas only 72.35% of TC was eliminated at pH 9.0. It could be attributed to the accelerated oxidation of iron in acidic conditions, resulting in the formation of abundant actived hydrogen atoms that facilitates the reduction of TC. When the pH value is higher than 7.0, an iron hydroxide passivation layer tends to form on the surfaces of Fe0 nanoparticles and CMBT, which inhibits the transport of TC and thus leads to a decrease in the removal rate of TC by the catalytic degradation.

Fig. 4
figure 4

Effect of pH (a), CM/BT mass ratio (b), initial concentration of TC (c) and temperature (d) on the removal performances of TC

Full size image

The effect of CM/BT mass ratio to the removal performances of TC was investigated. As shown in Fig. 4b, the removal rate of TC within 90.0 min is increased from 92.93% to 95.03% as the CM/BT mass ratio is changed from 1:0.2 to 1:0.4. However, the removal rate of TC is decreased to 90.33% when the BT mass ratio is further changed from 1:0.4 to 1:1. These results suggest that the transport of TC from the solution to the Fe0 nanoparticles is partially hindered by the formed dense layer of BT.

The influences of reaction temperature (288–303 K) on the removal performances of TC are shown in Fig. 4c. The removal rate of TC is enhanced with the increasing temperature. The removal rate of TC shows an increase from 93.68% to 97.28% when the temperature is increased from 288 to 303 K. As shown in Fig. 4d, the removal rate of TC is declined with the increase of initial concentration from 40.0 to 120.0 mg/L. The highest removal rate of TC was achieved at the initial concentration of 40.0 mg/L, which reached 95.03% within 90 min. However, only 75.86% of TC was degradated when the initial concentration of TC was 120.0 mg/L.

Figure 5a shows the removal performances of TC by using CMBT, commercial Fe0 nanoparticles and CMBT-Fe0, respectively, which obey the following order: CMBT-Fe0 > commercial Fe0 nanoparticles > CMBT. The CMBT shows quite limited removal performances to TC with ~ 2% of removal rate within 90 min, which manifests that Fe0 nanoparticles are indeed the active sites responsible for the degradation removal of TC. As for the commercial Fe0 nanoparticles (without the immobilization onto the CMBT), the corresponding removal rate of TC reaches 55.28% within 90 min. Compared with the commercial Fe0 nanoparticles, the CMBT-Fe0 provides considerably higher removal rate of TC, which is as high as 95.03% within 90 min, 1.72 times higher than that of the commercial Fe0 nanoparticles. Evidently, without the presence of CMBT, the Fe0 nanoparticles suffer from aggregation and/or oxidation, thus showing declined catalytic degradation removal of TC. Notably, compared with the previously reported Fe0 nanoparticle catalysts, the CMBT-Fe0 provides satisfied catalytic removal performances for the degradation of TC, as shown in Table 1.

Fig. 5
figure 5

Removal performances of TC by using CMBT, commercial Fe0 nanoparticles and CMBT-Fe0, respectively (a), cycling stability of CMBT-Fe0 for the catalytic removal of TC (b)

Full size image
Table 1 Comparisons of TC degradation performances between CMBT-Fe0 and other catalysts
Full size table

The reusability of CMBT-Fe0 for the degradation removal of TC was further investigated (Fig. 5b). During the recycles, the removal rate of TC was found to decrease gradually, while still maintaining at appreciable level. In the 6th cycle, the removal rate of TC still reaches 82.56%. These results manifest that the CMBT-Fe0 exhibited good cycling stability.

The intermediate products generated during the catalytic degradation removal of TC were analyzed by LC–MS (Additional file 1: Fig. S3). The degradation products were identified qualitatively, and the possible degradation route is shown in Fig. 6. The mass-to-charge ratio (m/z) of TC in the original solution is 444. As the degradation reaction progresses, the TC molecules are easily broken at the positions of C4 and C3 because of the low energy of the C–N bond, leading to the formation of the intermediate with the mass-to-charge ratio (m/z) of 381. After that, the cleavage of carboatomic ring A leads to the generation of the intermediate with the m/z of 305. The intermediate with the m/z of 275 is originated from the further decarboxylation reaction. The intermediate with the m/z of 245 is generated due to the subsequent dehydroxymethylation of the intermediate with an m/z of 275. Then, the cleavage of the hydroxyl in carboatomic ring B results in the formation of the intermediate with the m/z of 224. The intermediate with the m/z of 214 generates via the ring-opening reaction of carboatomic ring B. The intermediate products (with the m/z of 129 and 118) are observed as a result of losing some groups and benzene ring hydrogenation. As a consequence, the analyses to the intermediates suggest that the following reactions are involved during the catalytic degradation of tetracycline, including cleavage of carboatomic ring A, decarboxylation, dehydroxymethylation and hydrogenation of benzene ring [39, 40].

Fig. 6
figure 6

Schematic illustration showing the possible degradation pathway of TC

Full size image

4 Conclusions

In summary, the CMBT-Fe0 catalyst successfully developed by the inspiration of combination tanning mechanism displayed high activity and cycling stability for the catalytic removal of tetracycline. The CMBT-Fe0 was capable of providing the removal rate of TC as high as 95.03%, which was 1.72 times higher than that of commercial Fe0 nanoparticles without immobilization. The CMBT-Fe0 catalyst also showed satisfactory recycling performances, with 82.56% of removal rate to TC in the 6th cycle. Furthermore, a possible catalytic degradation removal mechanism was also proposed.

Availability of data and materials

All data from this study are presented in the paper and the supplementary material.

References

  1. Selmi T, Sanchez-Sanchez A, Gadonneix P, Jagiello J, Seffen M, Sammouda H, Celzard A, Fierro V. Tetracycline removal with activated carbons produced by hydrothermal carbonisation of Agave americana fibres and mimosa tannin. Ind Crop Prod. 2018;115:146–57. https://doi.org/10.1016/j.indcrop.2018.02.005.

    Article  CAS  Google Scholar 

  2. Liao Q, Rong H, Zhao M, Luo H, Chu Z, Wang R. Interaction between tetracycline and microorganisms during wastewater treatment: a review. Sci Total Environ. 2021;757:143981. https://doi.org/10.1016/j.scitotenv.2020.143981.

    Article  CAS  Google Scholar 

  3. Auerbach EA, Seyfried EE, McMahon KD. Tetracycline resistance genes in activated sludge wastewater treatment plants. Water Res. 2007;41:1143–51. https://doi.org/10.1016/j.watres.2006.11.045.

    Article  CAS  Google Scholar 

  4. Zhang P, Li Y, Cao Y, Han L. Characteristics of tetracycline adsorption by cow manure biochar prepared at different pyrolysis temperatures. Bioresour Technol. 2019;285:121348. https://doi.org/10.1016/j.scitotenv.2020.143981.

    Article  CAS  Google Scholar 

  5. Rigueto CVT, Rosseto M, Krein DDC. Alternative uses for tannery wastes: a review of environmental, sustainability, and science. Collagen Leather. 2020;2:21. https://doi.org/10.1186/s42825-020-00034-z.

    Article  Google Scholar 

  6. Wu S, Hu H, Lin Y, Zhang J, Hu Y. Visible light photocatalytic degradation of tetracycline over TiO2. Chem Eng J. 2020;382:122842. https://doi.org/10.1016/j.cej.2019.122842.

    Article  CAS  Google Scholar 

  7. Chang Q, Ali A, Su J, Wen Q, Bai Y, Gao Z. Simultaneous removal of nitrate, manganese, and tetracycline by Zoogloea sp. MFQ7: adsorption mechanism of tetracycline by biological precipitation. Bioresour Technol. 2021;340:125690. https://doi.org/10.1016/j.biortech.2021.125690.

    Article  CAS  Google Scholar 

  8. Fu Y, Peng L, Zeng Q, Yang Y, Song H, Shao J, Liu S, Gu J. High efficient removal of tetracycline from solution by degradation and flocculation with nanoscale zerovalent iron. Chem Eng J. 2015;270:631–40. https://doi.org/10.1016/j.cej.2015.02.070.

    Article  CAS  Google Scholar 

  9. Wang X, Zhang B, Ma J, Ning P. Novel synthesis of aluminum hydroxide gel-coated nano zero-valent iron and studies of its activity in flocculation-enhanced removal of tetracycline. J Environ Sci. 2020;89:194–205. https://doi.org/10.1016/j.jes.2019.09.017.

    Article  CAS  Google Scholar 

  10. Zha S, Cheng Y, Gao Y, Chen Z, Megharaj M, Naidu R. Nanoscale zero-valent iron as a catalyst for heterogeneous Fenton oxidation of amoxicillin. Chem Eng J. 2014;255:141–8. https://doi.org/10.1016/j.cej.2014.06.057.

    Article  CAS  Google Scholar 

  11. Xiao M, Qi W, Jia S, Pang M, Shi F, Mao H. High-performance removal of tetracycline enabled by Fe0 nanoparticles supported on carbon@ZIF-8. Chem Res Chin U. 2022;38(6):1349–55. https://doi.org/10.1007/s40242-022-2255-y.

    Article  CAS  Google Scholar 

  12. Nadagouda MN, Castle AB, Murdock RC, Hussain SM, Varm RS. In vitro biocompatibility of nanoscale zerovalent iron particles (NZVI) synthesized using tea polyphenols. Green Chem. 2010;12:114–22. https://doi.org/10.1039/B921203P.

    Article  CAS  Google Scholar 

  13. Astruc D. The supramolecular redox functions of metallomacromolecules. Collagen Leather. 2020;2:13. https://doi.org/10.1186/s42825-020-00026-z.

    Article  Google Scholar 

  14. Sun Z, Zheng S, Ayoko GA, Frostb RL, Xi Y. Degradation of simazine from aqueous solutions by diatomite-supported nanosized zero-valent iron composite materials. J Hazard Mater. 2013;263:768–77. https://doi.org/10.1016/j.jhazmat.2013.10.045.

    Article  CAS  Google Scholar 

  15. Baldermann A, Kaufhold S, Dohrmann R, Baldermann C, Letofsky-Papst I, Dietzel M. A novel nZVI–bentonite nanocomposite to remove trichloroethene (TCE) from solution. Chemosphere. 2021;282:131018. https://doi.org/10.1016/j.chemosphere.2021.131018.

    Article  CAS  Google Scholar 

  16. Chen H, Luo H, Lan Y, Dong T, Hu B, Wang Y. Removal of tetracycline from aqueous solutions using polyvinylpyrrolidone (PVP-K30) modified nanoscale zero valent iron. J Hazard Mater. 2011;192:44–53. https://doi.org/10.1016/j.jhazmat.2011.04.089.

    Article  CAS  Google Scholar 

  17. Wang X, Lian W, Sun X, Ma J, Ning P. Immobilization of NZVI in polydopamine surface-modified biochar for adsorption and degradation of tetracycline in aqueous solution. Front Env Sci Eng. 2018;12:1–11. https://doi.org/10.1007/s11783-018-1066-3.

    Article  CAS  Google Scholar 

  18. Dong H, Zhao F, He Q, Xie Y, Zeng Y, Zhang L, Tang L, Zeng G. Physicochemical transformation of carboxymethyl cellulose-coated zero-valent iron nanoparticles (nZVI) in simulated groundwater under anaerobic conditions. Sep Purif Technol. 2017;175:376–83. https://doi.org/10.1016/j.seppur.2016.11.053.

    Article  CAS  Google Scholar 

  19. Sun Y, Jing R, Zheng F, Zhang S, Jiao W, Wang F. Evaluating phytotoxicity of bare and starch-stabilized zero-valent iron nanoparticles in mung bean. Chemosphere. 2019;236:124336. https://doi.org/10.1016/j.chemosphere.2019.07.067.

    Article  CAS  Google Scholar 

  20. Sun M, Zhang Z, Liu G, Lv M, Feng Y. Enhancing methane production of synthetic brewery water with granular activated carbon modified with nanoscale zero-valent iron (NZVI) in anaerobic system. Sci Total Environ. 2021;760:143933. https://doi.org/10.1016/j.scitotenv.2020.143933.

    Article  CAS  Google Scholar 

  21. Yang Y, Xu L, Shen H, Wang J. Construction of three-dimensional reduced graphene oxide wrapped nZVI doped with Al2O3 as the ternary Fenton-like catalyst: Optimization, characterization and catalytic mechanism. Sci Total Environ. 2021;780:146576. https://doi.org/10.1016/j.scitotenv.2021.146576.

    Article  CAS  Google Scholar 

  22. Cirtiu CM, Raychoudhury T, Ghoshal S, Moores A. Systematic comparison of the size, surface characteristics and colloidal stability of zero valent iron nanoparticles pre-and post-grafted with common polymers. Colloid Surf A. 2011;390:95–104. https://doi.org/10.1016/j.colsurfa.2011.09.011.

    Article  CAS  Google Scholar 

  23. Nieto-Zambrano S, Ramos-Ramίrez E, Morales FT, Boffito DC, Naccache R, Ortega NLG, Litter MI, Cipagauta-Diaz S, Barbosa-Lopez AL. ZnAl hydrotalcites modified with nanocomposites nZVI–PAA for environmental remediation. J Mater Res Technol. 2021;14:2243–56. https://doi.org/10.1016/j.jmrt.2021.06.055.

    Article  CAS  Google Scholar 

  24. Kou SG, Peters LM, Mucalo MR. Chitosan: A review of sources and preparation methods. Int J Bio Macromol. 2021;169:85–94. https://doi.org/10.1016/j.ijbiomac.2020.12.005.

    Article  CAS  Google Scholar 

  25. Ahmed S, Ikram S. Chitosan based scaffolds and their applications in wound healing. Achiev Life Sci. 2016;10:27–37. https://doi.org/10.1016/j.als.2016.04.001.

    Article  Google Scholar 

  26. Ragetly GR, Griffon DJ, Lee HB, Chung YS. Effect of collagen II coating on mesenchymal stem cell adhesion on chitosan and on reacetylated chitosan fibrous scaffolds. J Mater Sci-Mater M. 2010;21:2479–90. https://doi.org/10.1007/s10856-010-4096-3.

    Article  CAS  Google Scholar 

  27. Yeul VS, Rayalu SS. Unprecedented chitin and chitosan: a chemical overview. J Polym Environ. 2013;21:606–14. https://doi.org/10.1007/s10924-012-0458-x.

    Article  CAS  Google Scholar 

  28. Zhang Z, Liu Y, Wang J, Xie T, Sun L, Li Z. A chrome-free combination tanning strategy: based on silicic acid and plant tannin. Collagen Leather. 2021;3:1–13. https://doi.org/10.1186/s42825-021-00058-z.

    Article  CAS  Google Scholar 

  29. Huang X, Wu H, Pu S, Liao X, Shi B. One-step room-temperature synthesis of Au@ Pd core–shell nanoparticles with tunable structure using plant tannin as reductant and stabilizer. Green Chem. 2011;13:950–7. https://doi.org/10.1039/C0GC00724B.

    Article  CAS  Google Scholar 

  30. Wang B, Sun J, Abbas M, Liu Y, Kong F, Xiao H, Chen J. A novel hydrothermal approach for the synthesis of flower-like Fe2O3/Fe foam nanocrystals and their superior performance in fisher–tropsch synthesis. Catal Lett. 2017;147:1153–61. https://doi.org/10.1016/j.carbon.2016.09.026.

    Article  CAS  Google Scholar 

  31. Pawlak A, Mucha M. Thermogravimetric and FTIR studies of chitosan blends. Thermochim Acta. 2003;396:153–66. https://doi.org/10.1016/S0040-6031(02)00523-3.

    Article  CAS  Google Scholar 

  32. Chupin L, Motillon C, Charrier-El Bouhtoury F, Pizzi A, Charrier B. Characterisation of maritime pine (Pinus pinaster) bark tannins extracted under different conditions by spectroscopic methods, FTIR and HPLC. Ind Crop Prod. 2013;49:897–903. https://doi.org/10.1016/j.indcrop.2013.06.045.

    Article  CAS  Google Scholar 

  33. Das PK, Mittra K, Dey A. Spectroscopic characterization of a phenolate bound Fe II–O2 adduct: gauging the relative “push” effect of a phenolate axial ligand. Chem Commun. 2014;50:5218–20. https://doi.org/10.1039/C3CC47528J.

    Article  CAS  Google Scholar 

  34. Ma Y, Wang B, Wang Q, Xing S. Facile synthesis of α-FeOOH/γ-Fe2O3 by a pH gradient method and the role of γ-Fe2O3 in H2O2 activation under visible light irradiation. Chem Eng J. 2018;354:75–84. https://doi.org/10.1016/j.cej.2018.08.011.

    Article  CAS  Google Scholar 

  35. Qin Q, Liu T, Zhang J, Wei R, You S, Xu Y. Facile synthesis of oxygen vacancies enriched α-Fe2O3 for peroxymonosulfate activation: a non-radical process for sulfamethoxazole degradation. J Hazard Mater. 2021;419:126447. https://doi.org/10.1016/j.jhazmat.2021.126447.

    Article  CAS  Google Scholar 

  36. Abdelfatah AM, Fawzy M, El-Khouly ME, Abdelazeem SE. Efficient adsorptive removal of tetracycline from aqueous solution using phytosynthesized nano-zero valent iron. J Saudi Chem Soc. 2021;12:101365. https://doi.org/10.1016/j.jscs.2021.101365.

    Article  CAS  Google Scholar 

  37. Wang X, Wang X, Lynch I, Ma J. High-efficiency removal of tetracycline from water by electrolysis-assisted NZVI: mechanism of electron transfer and redox of iron. RSC Adv. 2023;23:15881–91. https://doi.org/10.1039/D3RA00954H.

    Article  Google Scholar 

  38. Gopal G, Sankar H, Natarajan C, Mukherjee A. Tetracycline removal using green synthesized bimetallic nZVI-Cu and bentonite supported green nZVI-Cu nanocomposite: a comparative study. J Environ Manag. 2020;254:109812. https://doi.org/10.1016/j.jenvman.2019.109812.

    Article  CAS  Google Scholar 

  39. Cao J, Xiong Z, Lai B. Effect of initial pH on the tetracycline (TC) removal by zero-valent iron: adsorption, oxidation and reduction. Chem Eng J. 2018;343:492–9. https://doi.org/10.1016/j.cej.2018.03.036.

    Article  CAS  Google Scholar 

  40. Li Y, Sun X, Tang Y, Ng YH, Li L, Jiang F, Wang J, Chen W, Li L. Understanding photoelectrocatalytic degradation of tetracycline over three-dimensional coral-like ZnO/BiVO4 nanocomposite. Mater Chem Phys. 2021;271:124871. https://doi.org/10.1016/j.matchemphys.2021.124871.

    Article  CAS  Google Scholar 

Download references

Funding

This work was financially supported by National Key R&D Program of China (2021YFC2103800), the Technical Development Project of Sichuan University (No.22H0798) and Fundamental Research Funds for the Central Universities.

Author information

Authors and Affiliations

  1. College of Chemical Engineering, Sichuan University, Chengdu, 610065, People’s Republic of China

    Meng Xiao, Shuangmei Liu, Wenqian Qi & Hui Mao

  2. College of Chemistry and Materials Science, Sichuan Normal University, Chengdu, 610066, People’s Republic of China

    Yu Peng

  3. School of Materials Science and Engineering, Nanyang Technological University, Singapore, 639798, Singapore

    Qingyu Yan

Authors
  1. Meng Xiao
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Shuangmei Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Wenqian Qi
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Yu Peng
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Qingyu Yan
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Hui Mao
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

MX: Investigation, Methodology, Writing-original draft. SL: Investigation. WQ: Investigation. YP: Investigation, Methodology. QY: Writing-review, Methodology. HM: Conceptualization, Writing-review & editing, Supervision, Funding acquisition.

Corresponding author

Correspondence to Hui Mao.

Ethics declarations

Competing interests

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper. Qingyu Yan is a member of the editorial board of Collagen and Leather, and was not involved in the editorial review, or the decision to publish this article. All authors declare that there are no competing interests.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary Information

Additional file 1:

Fig. S1. Photographs of CM and CMBT after immersion in 0.2 mol/L HCl for 24 h. Fig. S2. XPS survey scan spectra of CMBT-Fe° before (a) and after (b) the degradation of TC. Fig. S3. Mass spectrum of TC (a), mass spectra of TC degraded by CMBT-Fe° for 30 min (b) and 90 min (c), respectively.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Xiao, M., Liu, S., Qi, W. et al. Combination tanning mechanism inspired environmentally benign catalyst for efficient degradation of tetracycline. Collagen & Leather 5, 22 (2023). https://doi.org/10.1186/s42825-023-00130-w

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s42825-023-00130-w

Keywords